Paint knowledge | wear resistant ceramic coating construction wear resistant ceramic coating formula

Core tip: wear resistant ceramic coating is a kind of non-metallic cementitious material It is a kind of powder ceramic material made of acid and alkali resistant synthetic raw materials by strict process ratio and advanced inorganic polymerization technology At the construction site, the special liquid inorganic glue is added to the material, which is applied to the inner lining or surface of the equipment manually or mechanically After a series of chemical reactions, the bonding strength and hardness of the ceramics are achieved three days later at normal temperature, so it is called wear-resistant ceramic coating Formula materials of wear-resistant ceramic coating: phosphoric acid, aluminum hydroxide, sulfuric acid, sodium hydroxide, anhydrous sodium sulfate, hydrated sodium phosphate ceramic aggregate I, ceramic aggregate II, magnesium oxide Resistance Paint knowledge how about Akzo Nobel Powder Coating Recommended introduction: powder coating is a kind of coating with different form from general coating, which is in powder form It is a new type of coating, because of its own advantages and more and more known by people Let's introduce Akzo Nobel Powder coating Akzo Nobel Powder coating is a cost-effective coating solution, which can be applied to different kinds of products After the treatment of static electricity and fire baking, a tough and durable coating surface will be formed, with the least impact on the environment Since the introduction of this technology, powder coating has been able to continue to maintain the Coating home news: wear resistant ceramic coating is a kind of non-metallic cementitious material It is a kind of powder ceramic material made of acid and alkali resistant synthetic raw materials through strict process proportion and advanced inorganic polymerization technology At the construction site, the special liquid inorganic glue is added to the material, which is applied to the inner lining or surface of the equipment manually or mechanically After a series of chemical reactions, the bonding strength and hardness of the ceramics are achieved three days later at normal temperature, so it is called wear-resistant ceramic coating Formula materials of wear-resistant ceramic coating: phosphoric acid, aluminum hydroxide, sulfuric acid, sodium hydroxide, anhydrous sodium sulfate, hydrated sodium phosphate ceramic aggregate I, ceramic aggregate II, magnesium oxide Aluminum dihydrogen phosphate is selected as the base material of wear-resistant and ceramic resistant coating The synthesis method is that phosphoric acid is reacted with aluminum hydroxide in a certain proportion at a certain temperature When the ratio of Al / P is 1:3.3 ~ 1.4:3 and the synthesis temperature is 120 ~ 140 ℃, aluminum dihydrogen phosphate matrix with excellent properties and high yield can be obtained When the ratio of aggregate to base material is 1.7:1, the wear resistance of the coating is better In the price of wear-resistant ceramic coating, the market price of wear-resistant ceramic coating is generally between 1500 yuan and 2500 yuan The market price of star wear-resistant ceramic coating is generally between 550 yuan and 650 yuan During the construction of wear-resistant ceramic coating, 1 Check that the temperature of the construction site must be controlled between 5 ℃ and 40 ℃ If the temperature is too low, the material itself and the construction area must be heated to 5 ℃ until the wear-resistant coating is applied However, construction under direct sunlight or strong wind shall be avoided to prevent rapid drying and cracking of wear-resistant coating surface 2 Conduct surface treatment A clean the surface of the anti-wear equipment to expose the bone structure to form a plate b Remove the loose materials and impurities on the surface completely C Weld and repair the inner wall of worn-out or near worn-out parts 3 The welding specification of tortoise shell net on the equipment surface is: 1.2mm * 15mm * 50mm * 50mm material is: A4 steel tortoise shell net, the tortoise shell net is welded by electric arc welding, and the weld length is 0.8mm Model: J422 electrode, (slag removal after welding) The average tensile strength of the solder joint is 320MPa, and the average compressive strength is 550MPa Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,