Fangxin FX-354 artificial stone basin resin.

Main characteristics and uses
FX-354 resin is benzene, shunyu and standard binary alcohol as the main raw material phthalates unsaturated polyester resin, has been dissolved in styrene and other cross-linked monomers, with medium viscosity and moderate reaction activity.
the resin has good colorability, high strength and good toughness. Suitable for solid surface materials, ordinary ware and other casting products

. Used to make face wash dressers, series of kitchen equipment, a variety of tables and service counter bottoms, wall materials, bathtubs, interior decoration materials and other artificial basin products.
liquid performance indicators
items
units
data
test standard
appearance
-
transparent white liquid
visual
viscosity
25 degrees C
Pa.Pa. s
0.45-0.55
GB/T 7193.1-2008
gelding time
25 degrees C
min
5-8
GB/T 7193.6-2008

%
%
63-69
GB/T 7193.3-2008
thermal stability
80C
H

>24
GB/T 7193.5-2008
Gel test conditions: 25 degrees C air bath 50g resin with 0.5 ml of cobalt isoic acid solution and 0.5 ml MEKP solution.
resin casting performance indicators
items
units
typical values
test standards
se
-
casting body without defects
visital
pasteur hardness
-

33 GB/T 3854-2005
thermal deformation temperature
degrees C
55
GB/T 1634-2004
break elongation
%


5.5
GB/T 2567-2008
Stretch Strength
Mpa
50
GB/T 2567-2008
Stretch Elastic Module

Mpa
2400
GB/T 2567-2008
BendIng Strength
Mpa
80
GB/T 2567-2008.
bending elastic module
. Mpa
2400
GB/T 2567-2008
Impact Strength
KJ/m2
10
GB/T 2567-2008
Product Instructions
1. FX-354 resins contain wax, promoter-free and tactinant-free additives.
2. FX-354 resins are suitable for ordinary solid surfaces and ordinary casting ware, FX-356 or FX-358 resins are recommended for higher yellowing performance requirements, and interbenzene-neodol-type FX-888IN or FX-355UV resins are recommended for higher water, weather and special-shaped processing.
3. Cutting and polishing in the production process should be carried out after full curing.
4. After curing at 60-70 degrees C for not less than 3 hours, the product performance is better.
5. Moisture absorption of fillers should be avoided, and excessive moisture content will affect the curing of products, resulting in reduced performance.
6. This information is based on GB7193 standards, according to the company's actual situation, combined with the needs of users prepared.
7. Because there are many variables in the use of the product, it is recommended that users test and test before using it.
8. Due to the increasing use of unsaturated polyester resins, certain properties of the product may not be fully applicable for a particular use. Our company reserves the right to modify certain technical parameters.
9. If the user on the required products and need to understand the problem can not be found in this information, please contact Fangxin company directly, Fangxin company will be based on the needs of users to do our best to provide services.
10. The unsaturated polyester resin products listed in this information are dangerous goods and shall be stored and transported in accordance with the relevant provisions of the State.
11. Liquid unsaturated polyester resin is unstable and should be stored in a cool place to avoid fire and isolate heat sources. The storage period below 25 degrees C is three months.
product packaging
unsaturated polyester resin with standard size iron barrel packaging, net weight of 220 kg.
.